(MPa) | Indirect tensile strength | Compressive strength | ||||||
---|---|---|---|---|---|---|---|---|
light-curing | autopolymerization | light-curing | autopolymerization | |||||
cement | 24 h | TC | 24 h | TC | 24 h | TC | 24 h | TC |
MLA | 55.3 (4.2)A | 43.9 (4.4)B | 51.3 (1.7)C | 41.1 (1.7)B | 343.8 (19.6)A | 326.3 (13.5)B | 321.0 (9.3)B | 300.5 (10.6)C |
MSC | 41.0 (2.2)A | 36.0 (3.0)B | 39.8 (2.9)A | 33.9 (3.2)B | 244.3 (11.0)A | 220.9 (8.9)B | 228.6 (12.7)B | 222.9 (13.5)B |
RUL | 46.0 (4.8)A | 38.0 (2.7)B | 33.7 (3.7)B | 39.2 (7.1)B | 293.5 (10.5)A | 286.6 (14.5)A | 238.8 (28.8)B | 301.7 (13.3)A |
RUN | 44.4 (4.7)A | 33.3 (5.1)B | 39.1 (3.6)A,B | 40.2 (7.6)A | 283.2 (17.3)A,B | 273.1 (28.2)A | 259.9 (20.8)A | 305.2 (11.5)B |
PV5 | 54.0 (3.2)A | 52.2 (4.6)A | 52.5 (5.0)A | 43.7 (4.2)B | 325.8 (12.3)A | 312.3 (6.6)A,B | 310.5 (15.2)B | 283.8 (13.2)C |
PSA | 49.5 (2.5)A | 37.4 (6.8)B | 38.2 (1.9)B | 40.9 (4.7)B | 297.8 (7.1)A | 300.8 (10.1)A | 263.9 (13.8)B | 267.3 (15.8)B |
HIS | 7.5 (1.4)A | 6.9 (1.0)A,B | 5.2 (0.8)C | 6.1 (1.0)B,C | 37.7 (3.3)A | 39.8 (1.8)A | 37.1 (7.0)A | 35.8 (1.8)A |