Table 1 Cement material composition provided by the manufacturer

From: Effect of aging and curing mode on the compressive and indirect tensile strength of resin composite cements

 

Name

Manufacturer

Type

Monomers

Fillers

Initiators

MLA

Multilink Automix

Ivoclar Vivadent

Adhesive resin composite

Base paste: Bis-GMA, HEMA, 2-dimethylaminoethyl methacrylate

Catalyst paste: ethyoxylated bisphenol A dimethacrylate, UDMA, HEMA

40 vol%

- Barium glass

- Ytterbium trifluoride

- Spheroid mixed oxide

Particle size: 0.25–3.0 μm

Dibenzoyl peroxide

MSC

Multilink Speed CEM

Ivoclar Vivadent

Self-adhesive resin composite

Base paste: UDMA, TEGDMA, polyethylene glycol dimethacrylate

Catalyst paste: polyethylene glycol dimethacrylate, TEGDMA, Methacrylated phosphoric acid ester, UDMA

40 vol%

- Barium glass

- Ytterbium trifluoride

Particle size: 0.1–7 μm

Dibenzoyl peroxide

RUL

RelyX Ultimate

3 M ESPE

Adhesive resin composite

Base paste: methacrylate monomers containing phosphoric acid groups, methacrylate monomers

Catalyst paste: methacrylate monomers

43 vol%

- Silanated fillers

- Alkaline (basic) fillers

Particle size: 13 μm

Sodium toluene-4-sulphinate,

Disodium peroxodisulphate,

Tert-butyl 3,5,5-trimethylperoxyhexanoate

RUN

RelyX Unicem 2 Automix

3 M ESPE

Self-adhesive resin composite

Base paste: phosphoric acid modified methacrylate monomers, bi-functional methacrylate

Catalyst paste: methacrylate monomers

43 vol%

- Alkaline (basic) fillers

- Silanated fillers

Particle size: 12.5 μm

Sodium toluene-4-sulphinate, Sodium Persulfate, Tert-butyl 3,5,5-trimethylperoxyhexanoate

PV5

Panavia V5

Kuraray

Adhesive resin composite

Paste A: Bis-GMA, TEGDMA, Hydrophobic aromatic dimethacrylate, Hydrophilic aliphatic dimethacrylate

Paste B: Bis-GMA, Hydrophobic aromatic dimethacrylate, Hydrophilic aliphatic dimethacrylate

38 vol%

- Silanated barium glass filler

- Silanated fluoroalminosilicate glass filler

- Colloidal silica

- Silanated alminium oxide filler

Particle size: 0.01–12 μm

dl-Camphorquinone

PSA

Panavia SA plus

Kuraray

Self-adhesive resin composite

Paste A: 10-MDP, Bis-GMA,

TEGDMA, Hydrophobic aromatic dimethacrylate, HEMA

Paste B: Hydrophobic aromatic dimethacrylate, hydrophobic aliphatic dimethacrylate

40 vol%

- Silanated barium glass filler

- Silanated colloidal silica

Particle size: 0.02–20 μm

dl-Camphorquinone

HIS

Harvard Implant semi-permanent

Harvard Dental International

temporary resin cement

Methacrylates, zinc oxide

  1. 10-MDP 10-Methacryloyloxydecyl dihydrogen phosphate, Bis-GMA bisphenol A-glycidyl methacrylate, HEMA 2-hydroxyethyl methacrylate, TEGDMA triethyleneglycol dimethacrylate, UDMA urethane dimethacrylate